Japan Industry Standard( JIS)
IS G3106 SM400A
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.23 | 0.25 | ~ | ≥2.5xC | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | >40 | |
245 | 235 | 215 | 215 | 205 | 195 | 400~510 | 400~510 | ≥23 | ≥18 | ≥22 | ≥24 |
JIS G3106 SM400C
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.18 | 0.18 | 0.35 | 1.4 | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | >40 | |
245 | 235 | 215 | 215 | - | - | 400~510 | 400~510 | ≥23 | ≥18 | ≥22 | ≥24 |
JIS G3106 SM400B
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.20 | 0.22 | 0.35 | 0.60-1.40 | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | >40 | |
245 | 235 | 215 | 215 | 205 | 195 | 400~510 | 400~510 | ≥23 | ≥18 | ≥22 | ≥24 |
JIS G3106 SM490A
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.20 | 0.22 | 0.55 | 1.6 | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | >40 | |
325 | 315 | 295 | 295 | 285 | 275 | 490-610 | 490-610 | ≥22 | ≥17 | ≥21 | ≥23 |
JIS G3106 SM490B
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.18 | 0.2 | 0.55 | 1.6 | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | >40 | |
325 | 315 | 295 | 295 | 285 | 275 | 490-610 | 490-610 | 22 | 17 | 21 | 23 |
JIS G3106 SM490C
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.18 | 0.18 | 0.55 | 1.6 | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | >40 | |
325 | 315 | 295 | 295 | - | - | 490-610 | 490-610 | ≥22 | ≥17 | ≥21 | ≥23 |
JIS G3106 SM490YA
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.20 | 0.20 | 0.55 | 1.6 | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | >40 | |
325 | 355 | 335 | 325 | - | - | 490-610 | - | 19 | 15 | 19 | 21 |
JIS G3106 SM490YB
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.20 | 0.20 | 0.55 | 1.6 | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | >40 | |
365 | 355 | 335 | 325 | - | - | 490-610 | - | 19 | 15 | 19 | 21 |
JIS G3106 SM520B
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.20 | 0.20 | 0.55 | 1.6 | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | >40 | |
365 | 355 | 335 | 325 | - | - | 520-640 | - | 19 | 15 | 19 | 21 |
JIS G3106 SM520C
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.20 | 0.20 | 0.55 | 1.6 | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | >40 | |
365 | 355 | 335 | 325 | - | - | 520-640 | - | 19 | 15 | 19 | 21 |
JIS G3106 SM570
Chemical composition % MAX | |||||||||||||
C | Si | Mn | P | S | |||||||||
TH(MM) | ≤50 | >50≤200 | |||||||||||
0.18 | 0.18 | 0.55 | 1.6 | 0.035 | 0.035 | ||||||||
Mechanical properties MIN | |||||||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | Elongation % | |||||||||||
TH(MM) | ≤16 | >16-40 | >40-75 | >75-100 | >100-160 | >160-200 | ≤100 | >100-200 | ≤15 | >5-16 | >16-50 | ||
460 | 450 | 430 | 420 | - | - | 570-720 | - | 19 | 26 | 20 |