Deutsche Intitut Norum( DIN)
DIN17100: RSt37-2, St52-3, DIN17102: StE315, StE355, StE370, StE420, StE469, TSeE315, WStE315, WStE500, EStE285, digunakan untuk struktur umum yaitu bangunan jembatan dan gedung.
Sedangan untuk selain struktur seperti mesin digunakan DIN17200.
Sedangan untuk selain struktur seperti mesin digunakan DIN17200.
DIN17100 RSt37-2
Chemical composition % MAX | |||||||||
C | Si | P | S | N2 | |||||
TH (MM) | ≤16 | >16≦32 | >32≦40 | >40 | |||||
0.17 | 0.17 | 0.17 | 0.20 | ~ | 0.05 | 0.05 | 0.009 | ||
Mechanical properties MIN | |||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | ||||||||
TH (MM) | ≤16 | >16≦40 | >40≦63 | >63≦80 | >80≦100 | >100 | <3 | >3≦100 | >100 |
235 | 225 | 215 | 215 | 215 | ~ | 360-510 | 340-470 | ~ |
DIN17100 St37-2
Chemical composition % MAX | |||||||||
C | Si | P | S | N2 | |||||
TH (MM) | ≤16 | >16 | |||||||
0.17 | 0.20 | - | 0.05 | 0.05 | 0.009 | ||||
Mechanical properties MIN | |||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | ||||||||
TH (MM) | ≤16 | >16≦40 | >40≦63 | >63≦80 | >80≦100 | >100 | <3 | >3≦100 | >100 |
235 | 225 | 215 | 205 | 195 | - | 360-510 | 340-470 | - |
DIN17100 RSt37-2
Chemical composition % MAX | |||||||||
C | Si | P | S | N2 | |||||
TH (MM) | ≤16 | >16≦32 | >32≦40 | >40 | |||||
0.17 | 0.17 | 0.17 | 0.20 | - | 0.05 | 0.05 | 0.009 | ||
Mechanical properties MIN | |||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | ||||||||
TH (MM) | ≤16 | >16≦40 | >40≦63 | >63≦80 | >80≦100 | >100 | <3 | >3≦100 | >100 |
235 | 225 | 215 | 215 | 215 | - | 360-510 | 340-470 | - |
DIN17100 St52-3
Chemical composition % MAX | |||||||||
C | Si | P | S | N2 | |||||
TH (MM) | ≤16 | >16≦32 | >32≦40 | >40 | |||||
0.20 | 0.20 | 0.22 | 0.22 | - | 0.05 | 0.05 | 0.009 | ||
Mechanical properties MIN | |||||||||
Yield strength (N/MM2) | Tensile strength (N/MM2) | ||||||||
TH (MM) | ≤16 | >16≦40 | >40≦63 | >63≦80 | >80≦100 | >100 | <3 | >3≦100 | >100 |
355 | 345 | 335 | 325 | 315 | - | 510-680 | 490-630 | - |
DIN17102 StE315
S% max | N% max | Al % max | Cr % max | Cu % max | Mo % max | Ni % | Nb % max | ||||||||
0.03 | 0.2 | 0.2 | 0.3 | 0.20 | 0.08 | 0.3 | 0.03 | ||||||||
Tensile strength Mpa min | Yield Strength Mpa Min | ||||||||||||||
440-560 | 430-550 | 420-540 | 410-530 | 400-520 | 315 | 315 | 305 | 295 | 295 | 285 | 275 | 265 | 255 | 23 |
DIN17102 EStE285
S% max | N% max | Al % max | Cr % max | Cu % max | Mo % max | Ni % | Nb % max | ||||||||
0.015 | 0.2 | 0.2 | 0.3 | 0.20 | 0.08 | 0.3 | 0.03 | ||||||||
Tensile strength Mpa min | Yield Strength Mpa Min | ||||||||||||||
440-560 | 430-550 | 420-540 | 410-530 | 400-520 | 285 | 285 | 276 | 265 | 265 | 255 | 245 | 235 | 225 | 24 |
DIN17102 TStE315
S% max | N% max | Al % max | Cr % max | Cu % max | Mo % max | Ni % | Nb % max | ||||||||
0.025 | 0.2 | 0.2 | 0.3 | 0.20 | 0.08 | 0.3 | 0.03 | ||||||||
Tensile strength Mpa min | Yield Strength Mpa Min | ||||||||||||||
440-560 | 430-550 | 420-540 | 410-530 | 400-520 | 315 | 315 | 305 | 295 | 295 | 285 | 275 | 265 | 255 | 23 |
DIN17102 WStE315
S% max | N% max | Al % max | Cr % max | Cu % max | Mo % max | Ni % | Nb % max | ||||||||
0.03 | 0.2 | 0.2 | 0.3 | 0.20 | 0.08 | 0.3 | 0.03 | ||||||||
Tensile strength Mpa min | Yield Strength Mpa Min | ||||||||||||||
440-560 | 430-550 | 420-540 | 410-530 | 400-520 | 315 | 315 | 305 | 295 | 295 | 285 | 275 | 265 | 255 | 23 |
DIN17102 StE355
S% max | N% max | Al % max | Cr % max | Cu % max | Mo % max | Ni % | Nb % max | ||||||||
0.03 | 0.2 | 0.2 | 0.3 | 0.20 | 0.1 | 0.3 | 0.05 | ||||||||
Tensile strength Mpa min | Yield Strength Mpa Min | ||||||||||||||
490-630 | 480-620 | 470-610 | 460-600 | 460-590 | 355 | 355 | 345 | 335 | 335 | 325 | 315 | 305 | 295 | 22 |
DIN17102 StE380
S% max | N% max | Al % max | Cr % max | Cu % max | Mo % max | Ni % | Nb % max | ||||||||
0.03 | 0.2 | 0.2 | 0.3 | 0.20 | 0.1 | 1.0 | 0.05 | ||||||||
Tensile strength Mpa min | Yield Strength Mpa Min | ||||||||||||||
500-650 | 490-640 | 480-630 | 470-620 | 460-610 | 380 | 375 | 365 | 355 | 345 | 335 | 325 | 315 | 305 | 20 |
DIN17102 StE420
S% max | N% max | Al % max | Cr % max | Cu % max | Mo % max | Ni % | Nb % max | ||||||||
0.03 | 0.2 | 0.2 | 0.3 | 0.20 | 0.1 | 1.0 | 0.05 | ||||||||
Tensile strength Mpa min | Yield Strength Mpa Min | ||||||||||||||
530-680 | 520-670 | 510-660 | 500-650 | 460-640 | 420 | 410 | 400 | 390 | 385 | 375 | 365 | 355 | 345 | 19 |
DIN17102 StE460
S% max | N% max | Al % max | Cr % max | Cu % max | Mo % max | Ni % | Nb % max | ||||||||
0.03 | 0.2 | 0.2 | 0.3 | 0.20 | 0.1 | 1.0 | 0.05 | ||||||||
Tensile strength Mpa min | Yield Strength Mpa Min | ||||||||||||||
560-730 | 550-720 | 540-710 | 530-700 | 520-690 | 460 | 450 | 440 | 430 | 420 | 410 | 400 | 390 | 380 | 17 |
DIN17102 WStE500
S% max | N% max | Al % max | Cr % max | Cu % max | Mo % max | Ni % | Nb % max | ||||||||
0.03 | 0.2 | 0.2 | 0.3 | 0.20 | 0.1 | 1.0 | 0.05 | ||||||||
Tensile strength Mpa min | Yield Strength Mpa Min | ||||||||||||||
610-780 | 600-770 | 590-760 | 580-750 | 570-740 | 500 | 480 | 470 | 460 | 450 | 440 | 430 | 420 | 410 | 18 |